Příprava a analýza tenkých vrstev slitin s vysokou entropií nanesených metodou Ionized Jet Deposition
Preparation and analysis of High Entropy Alloys thin films deposited by Ionized Jet Deposition method
Typ dokumentu
bakalářská prácebachelor thesis
Autor
Jáchym Lis
Vedoucí práce
Skočdopole Jakub
Oponent práce
Čapek Jiří
Studijní obor
Inženýrství pevných látekStudijní program
Aplikace přírodních vědInstituce přidělující hodnost
katedra inženýrství pevných látekObhájeno
2023-08-29Práva
A university thesis is a work protected by the Copyright Act. Extracts, copies and transcripts of the thesis are allowed for personal use only and at one?s own expense. The use of thesis should be in compliance with the Copyright Act http://www.mkcr.cz/assets/autorske-pravo/01-3982006.pdf and the citation ethics http://knihovny.cvut.cz/vychova/vskp.htmlVysokoškolská závěrečná práce je dílo chráněné autorským zákonem. Je možné pořizovat z něj na své náklady a pro svoji osobní potřebu výpisy, opisy a rozmnoženiny. Jeho využití musí být v souladu s autorským zákonem http://www.mkcr.cz/assets/autorske-pravo/01-3982006.pdf a citační etikou http://knihovny.cvut.cz/vychova/vskp.html
Metadata
Zobrazit celý záznamAbstrakt
Cílem této bakalářské práce byl výzkum přípravy tenkých vrstev slitin s vysokou entropií pomocí metody Ionized jet deposition. V teoretické části jsou popsány slitiny s vysokou entropií, dále je představena metoda IJD a krátce jsou popsány další v práci použité analytické metody. V experimentální části práce je popsána příprava terčíku pro nanášení slitiny FeNiCoCuCr metodou IJD. Z tohoto terčíku bylo následně naneseno celkem šest vrstev, z čehož byly dvě testovací a následné čtyři byly zaměřené na studium vlivu nanášecího napětí. Tato série čtyř vzorků byla analyzována pomocí metod AFM, SEM, EDS a XRD za účelem stanovení tloušťky vrstev, homogenity povrchu, prvkového a fázového složení a jejich závislosti na nanášecím napětí. Analýzy ukázaly s rostoucím nanášecím napětím klesající tloušťku vrstvy, mírně klesající homogenitu, přibližně konstantní prvkové složení a obsah FCC fází s malým podílem oxidů. Zároveň byl ve vrstvách i terčíku zjištěn obsah kyslíku. V dalším výzkumu by bylo vhodné se zaměřit na zvýšení homogenity vrstev a úpravu jejich prvkového složení, zejména odstranění kyslíku. The aim of this bachelor thesis was to investigate the preparation of high-entropy alloys thin films using the Ionized Jet Deposition method. In the theoretical part, high-entropy alloys are described, the IJD method is introduced and other analytical methods used in the thesis are briefly explained. In the experimental part of the thesis the preparation of the target for deposition of FeNiCoCuCr alloy by IJD method is described. A total of six layers were subsequently deposited from this target, two of which were test layers and the subsequent four were aimed at studying the effect of the deposition voltage. This series of four samples was analysed by AFM, SEM, EDS and XRD to determine the layer thickness, surface homogeneity, elemental and phase composition and their dependence on the deposition voltage. The analyses showed decreasing layer thickness, slightly decreasing homogeneity and approximately constant elemental composition with increasing deposition voltage and FCC content of phases with a small proportion of oxides. At the same time, the oxygen content was detected both in the layers and target. Future research should focus on increasing the homogeneity of the layers and modifying their elemental composition, especially the removal of oxygen.
Kolekce
Související záznamy
Zobrazují se záznamy příbuzné na základě názvu, autora a předmětu.
-
Řízení robotu pro zajištění kvalitní technologie navařování
Autor: Martin Novák; Vedoucí práce: Brajer Jan; Oponent práce: Mrňa Libor
(České vysoké učení technické v Praze. Vypočetní a informační centrum.Czech Technical University in Prague. Computing and Information Centre., 2022-08-26)Diplomová práce se zabývá řízením robotu realizujícího technologii koaxiálního navařování z drátu pomocí laseru. V rámci práce jsou porovnány aditivní technologie pro výrobu z kovu. Jsou představeny výhody a nevýhody robotu ... -
Fouling in process apparatuses
Autor: Kumar Gautam Rahul; Vedoucí práce: Dostál Martin; Oponent práce: Štancl Jaromír
(České vysoké učení technické v Praze. Vypočetní a informační centrum.Czech Technical University in Prague. Computing and Information Centre., 2018-01-12)This resesrch work contain the brief discription of fouling, types of fouling and the mechanism by which it create on the surface of heat exchangers. Mainly the thesis work focus on the fouling in food process industries ... -
Technologie 3D tisku
Autor: Vích Ondřej; Vedoucí práce: Jeníková Zdeňka; Oponent práce: Pinkner Adam
(České vysoké učení technické v Praze. Vypočetní a informační centrum.Czech Technical University in Prague. Computing and Information Centre., 2018-09-05)Bakalářská práce nabízí přehled nejpoužívanějších technologií 3D tisku a zabývá se hodnocením vlivu nastavení různých parametrů při tisku metodou FDM na mechanické vlastnosti výrobku z materiálu PET-G. Zvolené měněné ...