Aluminium modification as indicator for current filaments under repetitive short-circuit in 650 V IGBTs
Typ dokumentu
conference paperstať ve sborníku
Autor
Madhu-Lakshman Mysore
Basler, Thomas
Lutz, Josef
Baburske, Roman
Schulze, Hans-Joachim
Niedernostheide, Franz-Josef
Metadata
Zobrazit celý záznamAbstrakt
In this work, an investigation of the top-side aluminium (Al) metallization modification, under repetitive
short-circuit (SC) type I measurements, was carried out for 650 V IGBTs. These measurements were
performed far beyond the safe operating area (SOA). The presence of current density filaments at the
collector side during SC leads to a local temperature increase that reconstructs the emitter metallization
and thus leads to a modification of the top Al surface. Here, the optical microscope was used to observe
the change in emitter surface metallization. For 650 V IGBTs, a uniform Al modification pattern was
observed irrespective of DC-link voltage and SC pulse width, which is in contrast to the results of 1200 V
and 1700 V IGBTs. The computer-aided TCAD simulations were performed using a simplified front-side
IGBT structure to understand the uniform Al modification on all the measured DC-link voltages.