JOINIG OF MG ALLOY AZ31B BY SELECTED TECHNOLOGIES
Typ dokumentu
articlePeer-reviewed
publishedVersion
Autor
Kramár , Tomáš
Vondrouš , Petr
Jáňa , Miroslav
Kupec , Tomáš
Práva
Creative Commons Attribution 4.0 International Licensehttp://creativecommons.org/licenses/by/4.0/
openAccess
Metadata
Zobrazit celý záznamAbstrakt
This contribution presents metallurgical joining of Mg alloy AZ 31B by several technologies - Friction Stir Welding - FSW, Laser Beam Welding - LBW, soldering and their mutual comparison. The difficulty of joining Mg alloys is connected with the strong MgO layer, low ductility of the weld metal (WM), a presence of intermetallic phases connected with the hardness increase. To successfully join Mg alloys, a precise setting of welding parameters is needed. The welds are susceptible to low mechanical properties as all samples fractured at WM. From the tested methods, laser beam welding proved the best results, because laser welding is the fastest and weld strength reached the highest values, i.e. 87% of BM (base metal) strength.
Kolekce
K tomuto záznamu jsou přiřazeny následující licenční soubory:
Kromě případů, kde je uvedeno jinak, licence tohoto záznamu je Creative Commons Attribution 4.0 International License