Equivalent thermal diffusivity of natural and recycled aggregate concrete at temperature up to 350 ⁰C
Typ dokumentu
articlePeer-reviewed
publishedVersion
Autor
Hager, Izabela
Mróz, Katarzyna
Tracz, Tomasz
Kočí, Václav
Fiala, Lukáš
Práva
Creative Commons Attribution 4.0 International Licensehttp://creativecommons.org/licenses/by/4.0/
openAccess
Metadata
Zobrazit celý záznamAbstrakt
The paper presents the evolution of equivalent thermal diffusivity with temperature of concretes with natural coarse aggregates and recycled concrete aggregates. Thermal diffusivity was evaluated based on the temperature measurements made on cylindrical samples using so-called "inverse technique". Thermal diffusivity parameter was estimated for concretes manufactured with different replacement ratios of natural by recycled coarse aggregate (0, 50 and 100 %) produced by crushing the worn-out concrete pavement that was dismounted after exploitation period. The diffusivity of concrete was tested up to 350 ◦C. The progressive decrease of thermal diffusivity was observed, and the lowest D values were obtained for higher recycled concrete aggregates content. The results were presented against the background of other authors results and referred to the D values proposed in EUROCODE 2.
Kolekce
K tomuto záznamu jsou přiřazeny následující licenční soubory:
Kromě případů, kde je uvedeno jinak, licence tohoto záznamu je Creative Commons Attribution 4.0 International License