MICROSTRUCTURE AND MICROHARDNESS EVALUATION FOR NiCrAlY MATERIALS MANUFACTURED BY SPARK PLASMA SINTERING AND PLASMA SPRAYING
Typ dokumentu
articlePeer-reviewed
publishedVersion
Autor
Hulka, Iosif
Mušálek, Radek
Lukáč, František
Klečka, Jakub
Chrástka, Tomáš
Práva
Creative Commons Attribution 4.0 International Licensehttp://creativecommons.org/licenses/by/4.0/
openAccess
Metadata
Zobrazit celý záznamAbstrakt
NiCrAlY deposited by different thermal spraying methods is commonly used as the bond coat material in thermal barrier coatings (TBCs). In the present study, two experimental coatings were deposited by hybrid water stabilized plasma (WSP-H) and radio frequency inductively coupled plasma (RF-ICP) using the same feedstock powder. Spark plasma sintering (SPS) was used to manufacture a compact NiCrAlY from the same feedstock powder as a reference material. Microstructure, internal oxidation, phase characterization and quantification of the mechanical behaviour in terms of microhardness were studied. The investigations clearly showed microstructural and mechanical differences between the NiCrAlY samples manufactured by different plasma technologies. The results confirmed that SPS and RF-ICP provide dense structures with no oxides due to the fabrication under protective atmosphere and similar mechanical properties. Thus, RF-ICP may be used for deposition of very dense coatings with microstructure and hardness comparable to compacted materials prepared by SPS.
Kolekce
K tomuto záznamu jsou přiřazeny následující licenční soubory:
Kromě případů, kde je uvedeno jinak, licence tohoto záznamu je Creative Commons Attribution 4.0 International License