EVALUATION OF INTERNAL COHESION OF MULTIPHASE PLASMA-SPRAYED COATINGS BY CAVITATION TEST: FEASIBILITY STUDY
Type of document
articlePeer-reviewed
publishedVersion
Author
Mušálek, Radek
Nardozza, Emanuele
Tesař, Tomáš
Medřický, Jan
Rights
Creative Commons Attribution 4.0 International Licensehttp://creativecommons.org/licenses/by/4.0/
openAccess
Metadata
Show full item recordAbstract
Mechanical characterization of plasma-sprayed coatings at microscopic level represents a major challenge due to the presence of numerous inherent microstructural features such as cracks, pores, or splat boundaries, which complicate coatings characterization by conventional testing methods. Need for reliable testing of structural integrity of newly developed multiphase plasma-sprayed coatings introduced even more complexity to the testing. In this study, applicability of indirect vibratory cavitation test (adapted from ASTM G32 standard) for such testing was evaluated. Three plasmasprayed coatings having distinctive microstructures were tested: i) conventional alumina coating deposited from coarse powder, ii) hybrid coating deposited by co-spraying of coarse alumina powder and fine yttria-stabilized zirconia (YSZ) suspension, and iii) compact alumina coating deposited from fine ethanol-based suspension. Differences in the coatings internal cohesion were reflected in different failure mechanisms observed within the cavitation crater by scanning electron microscopy and mean erosion rates being i) 280 μm/hour, ii) 97 μm/hour and iii) 14 μm/hour, respectively.
Collections
The following license files are associated with this item:
Except where otherwise noted, this item's license is described as Creative Commons Attribution 4.0 International License