SURFACE TREATMENT AND EXAMINATION OF GRADE 2 AND GRADE 5 TITANIUM
Type of document
articlePeer-reviewed
publishedVersion
Author
Nagy, Peter
Weszl, Miklos
Toth, Krisztian Laszlo
Kientzl, Imre
Ring, Gyorgy
Szabadits, Peter
Bognar, Eszter
Rights
Creative Commons Attribution 4.0 International Licensehttp://creativecommons.org/licenses/by/4.0/
openAccess
Metadata
Show full item recordAbstract
Surface characteristics play an important role in the implant-bone integration that is required for the long-term reliability of dental and orthopedic implants. In this paper, we investigate the effect of acid etching on the mass reduction and roughness of grade 2 and grade 5 Ti under controlled experimental conditions. Three different etching compounds were investigated: 30% HCl, 85% H3PO4 and the compound of 30% (COOH)2 × 2H2O and 30% H2O2 in various treatment intervals under controlled temperature. Stereo microscopy, scanning electron microscopy, roughness and weight measurements were carried out on the samples. We found that neither 85% H3PO4 nor the compound of 30% (COOH)2 × 2H2O and 30% H2O2 were able to remove the machining marks from the surface of Ti discs in our experimental setting. On the other hand, etching in 30% HCl yielded even surfaces both on Ti grade 2 and 5 discs. We also found that etching at higher temperatures in 30% HCl resulted in significant mass loss.
Collections
The following license files are associated with this item:
Except where otherwise noted, this item's license is described as Creative Commons Attribution 4.0 International License